Abstract:
This study aimed to investigate amount of γ-methacryloxypropyltrimethoxysilane (MPS) silanized on experimental nanosilica particles (NPs), amount of NPs and amount of MPS silanized NP on flexural strength (FS), flexural modulus (FM), and fracture toughness (FT) of NP reinforced polymethymethacrylate (PMMA). The chemisorbed amount of MPS was determined using elemental analysis. Six groups (n=8) were prepared with chemisorbed amount and mixed with PMMA-monomer to make 0.25, 0.5, 1, 5, 10 and 15% (w/w) of NP reinforced PMMA. PMMA without NP served as control. Seven groups (n=8) were prepared with 1% of NPs silanized with 0, 0.061, 0.123, 0.246, 0.493, 0.987, and 1.974 gMPS/gsilica and mixed with PMMA-monomer to make NPs reinforced PMMA. FS, FM, and FT were determined using 3-point bending test. One-way ANOVA and multiple comparisons showed that 0.246 gMPS/gsilica of 1% amount of silanized NP group was significantly highest in FS, FM, and FT compared to the others (p<0.05).